- Electropolishing Case Study: Titanium Parts for the Medical Industry
- Electropolishing Case Study: Surgical assembly used in tracheal procedures. The parts needed high corrosion resistance to corrosive sterilization chemicals.
- Electropolishing Case Study: Steel spring with surfaces too rough and contaminated to accept plating. Plating was peeling causing a high reject rate.
- Electropolishing Case Study: Stainless tubing assembly used in food application. Special masking of heating element was required to prevent damage.
- Electropolishing Case Study: Stainless Steel Weldment Used in a Critical Semiconductor Application
- Electropolishing Case Study: Stainless Steel Weldment
- Electropolishing Case Study: Stainless Steel & Brass Assembly with Braze & Flux Contamination
- Electropolishing Case Study: Stainless stamping used in automotive application needing improved corrosion resistance
- Electropolishing Case Study: Stainless stamping used in a corrosive battery application. Part also needed deburring on complex surfaces.
- Electropolishing Case Study: Stainless stamping used in a consumer knife assembly with interior burr problems.
- Electropolishing Case Study: Stainless stamping needing critical reflective surface for ultraviolet application
- Electropolishing Case Study: Stainless medical rack needing high corrosion resistance. Part is immersed in hot water for long periods.
- Electropolishing Case Study: Stainless food frying assembly needing high corrosion resistance and improved cleanability.
- Electropolishing Case Study: Stainless EDM part with recast layer problems
- Electropolishing Case Study: Stainless drawn part used in water fountain application. Parts needed to be bright and corrosion resistant.
- Electropolishing Case Study: Stainless air flow valve used in oxygen application needing a clean burr-free surface.
- Electropolishing Case Study: Springs subjected to a chlorine environment. Needed highly corrosion-resistant surface.
- Electropolishing Case Study: Semiconductor immersion heater with surface contamination needing to pass high standard testing.
- Electropolishing Case Study: Removing Heat Tint & Eliminating Heat Treat Side Effects
- Electropolishing Case Study: Piston Assembly Components Needing Surface Improvements
- Electropolishing Case Study: Pharmaceutical machined part needing a surface that would not harbor bacteria.
- Electropolishing Case Study: Optics Component Needing Decontamination
- Electropolishing Case Study: Nickel Silver medical part needing removal of surface contaminates caused by a brazing operation.
- Electropolishing Case Study: Multi-alloy medical part needing removal of surface contamination.
- Electropolishing Case Study: Multi-alloy assembly used in medical application needing purification
- Electropolishing Case Study: Micro Deburring & Surface Finish Improvement
- Electropolishing Case Study: Medical part used in oxygen metering needing precise finish improvement
- Electropolishing Case Study: Medical Casting Needing to Withstand Cleaning Agents Containing Bleach
- Electropolishing Case Study: Machined steel gear needing surface improvement for noise reduction
- Electropolishing Case Study: Machined Roller Surface Needing Smoothing After Shot Blasting
- Electropolishing Case Study: Machined parts that are oversized and rejected
- Electropolishing Case Study: Machined Parts Needed Brightening without Part Damage
- Electropolishing Case Study: Machined Part Needing Clean Surfaces in Complex Recesses
- Electropolishing Case Study: Machined medical part wearing due to metal-to-metal contact
- Electropolishing Case Study: Machined Casting Used in a Beverage Filling Application
- Electropolishing Case Study: Machined brass assembly used in industrial spraying application. The customer was looking to replace a destructive bright dip operation.
- Electropolishing Case Study: Large stainless weldment used in semiconductor chip fabrication. Part needed clean, chromium rich surfaces.
- Electropolishing Case Study: Large stainless hopper with powdered food adhesion problems
- Electropolishing Case Study: Large automotive part used in high vacuum leak testing application. The 1500 pound part needed high corrosion resistance.
- Electropolishing Case Study: Internal gear teeth required resizing due to growth caused by heat.
- Electropolishing Case Study: Improving 440C Stainless Steel Corrosion Resistance
- Electropolishing Case Study: Immersion heater made from tubular stainless needing improved corrosion resistance.
- Electropolishing Case Study: Heat treated tool steel part used in plastic molding application. Customer was looking to remove burrs and improve mold release characteristics.
- Electropolishing Case Study: Heat treated stamping needing both brightening and improved corrosion resistance
- Electropolishing Case Study: Heat treated part used in packaging machinery. Galling and other problems in teeth caused binding in the assembly.
- Electropolishing Case Study: Heat treated casting used in critical aerospace guidance system
- Electropolishing Case Study: Ground stainless surface needing fine burr removal. Part used in consumer appliances
- Electropolishing Case Study: Formed Tubes Needing Surface Contaminants Removed
- Electropolishing Case Study: Formed and welded 430 stainless panel used in computer application, needing contamination free surface.
- Electropolishing Case Study: Food/beverage component needing high corrosion resistance to cleaning chemicals.
- Electropolishing Case Study: Food Service Wireform
- Electropolishing Case Study: Food Processing Bushing
- Electropolishing Case Study: Food equipment with welding contamination
- Electropolishing Case Study: Food Application Assembly Needing High Corrosion Resistance
- Electropolishing Case Study: Fluid Control Valve Needle
- Electropolishing Case Study: Flat stamping that needs a bright surface without distortion or damage
- Electropolishing Case Study: Fasteners used for structural steel fabrication, transportation, OEMs & more
- Electropolishing Case Study: Fastener needing removal of heat treat discoloration
- Electropolishing Case Study: Extruded and machined brass part needing burr removal from complex surfaces.
- Electropolishing Case Study: Deburring Stainless Steel Medical Devices
- Electropolishing Case Study: Deburring a Stainless Steel Medical Part with Small Holes
- Electropolishing Case Study: Copper switch component with fine burrs causing pre-mature failure
- Electropolishing Case Study: Copper Stamping with Surface Contamination & Burrs
- Electropolishing Case Study: Copper stamping used in electronic assembly needing safe removal of fine burrs
- Electropolishing Case Study: Copper drawn part used in Aerospace oxygen application. Part needed clean surfaces free of contamination.
- Electropolishing Case Study: Copper automotive stamping with burrs that cut into a plastic mating surface.
- Electropolishing Case Study: Computer Component Needing Surface Improvement on Opposing Surfaces
- Electropolishing Case Study: Components of a fluid control system experienced corrosion. Parts needed improved corrosion resistance.
- Electropolishing Case Study: Complex welded and formed assembly with contamination from welding
- Electropolishing Case Study: Complex stainless machined part needing corrosion protection
- Electropolishing Case Study: Complex Shaft Assembly Used in Kidney Dialysis
- Electropolishing Case Study: Complex Machined Casting Needing Surface Cleaning without Part Damage
- Electropolishing Case Study: Complex Assembly of Multiple Alloys Needing Improved Sealing Surface
- Electropolishing Case Study: Clean Room Component Needing Contaminant-Free Metal Surface
- Electropolishing Case Study: Brazed Medical Assembly Needing Careful Cleaning
- Electropolishing Case Study: Brass nozzle with difficult burr located in orifice. The part is used in a beverage application.
- Electropolishing Case Study: Automotive stainless fastener needing high corrosion resistance.
- Electropolishing Case Study: Automotive fasteners needing removal of copper coating
- Electropolishing Case Study: Automotive fastener needing improved corrosion resistance
- Electropolishing Case Study: Automotive casting used in critical painting application. Part needed high corrosion resistance.
- Electropolishing Case Study: Aluminum reflector needing improved reflective properties. The part needed surface smoothing without damage to part geometry.
- Electropolishing Case Study: Aluminum reflector needing bright reflective finish
- Electropolishing Case Study: Aluminum mold used to form automotive hoses. Part needed a clean surface.
- Electropolishing Case Study: Aluminum forging with high hand-finishing costs. Electropolishing improved surface finishes and reduced costs.
- Electropolishing Case Study: Aluminum Component Used in a Cellular Application
- Electropolishing Case Study: Aluminum Bronze fastener used in electronic application. The part needed to meet semiconductor cleanliness specifications.
- Electropolishing Case Study: Aluminum aircraft reflector needing uniform improvement of parabolic areas.
- Electropolishing Case Study: Aircraft Seal Cleaning & Improved Corrosion Protection
- Electropolishing Case Study: A part used to mold implant devices. The machined surfaces needed smoothing prior to a critical plating operation.
- Cellular Phone Antenna Needing High Corrosion Resistance
- Case Study: Electropolishing Stainless Steel Springs for Increased Endurance
- 1091 – Aluminum lock rod used for tractor trailers.
- 1090 – Weldment used in commercial ice making system. Part needed economical cleaning of weld discoloration.
- 1089 – Stainless assembly used in complex printing machinery. Surfaces needed smoothing without damage to base part.
- 1088 – Stainless animal containment fabricated from formed wire. Part needed economical brightening and improved corrosion resistance.